ass1: Add T_c vs rho diagram, draft other questions
This commit is contained in:
@ -13,7 +13,7 @@
|
||||
pages = {17--27},
|
||||
}
|
||||
|
||||
@book{smidt,
|
||||
@book{schmidt,
|
||||
address = {Berlin},
|
||||
title = {The {Physics} of superconductors: introduction to fundamentals and applications},
|
||||
isbn = {9783642082511},
|
||||
|
||||
@ -31,7 +31,8 @@ df = pd.DataFrame(
|
||||
['Hf', .38, 340., '[webb]', '[crc]'],
|
||||
['Ir', .1, 47., '[webb]', 'at 273 K [crc]'],
|
||||
['Lu', .1, 582., '[webb]', '[crc]'],
|
||||
['Be', 1440, 37.6, '[webb]', '[crc]'],
|
||||
#['Be', 1440, 37.6, '[webb]', '[crc]'],
|
||||
['Be', .026, 37.6, '[schmidt] (but [webb] reports 1440 K)', '[crc]'],
|
||||
['W', .01, 54.4, '[webb]', '[crc]'],
|
||||
['Li', .0004, 95.5, '[webb]', '[crc]'],
|
||||
['Rh', .0003, 43., '[webb]', 'at 273 K [crc]'],
|
||||
@ -47,3 +48,15 @@ table = re.sub(r'\[(\w+)\]', r'\\cite{\1}', table)
|
||||
|
||||
with open('sc_elements.tex', 'w') as table_file:
|
||||
table_file.write(table)
|
||||
|
||||
from matplotlib import pyplot as plt
|
||||
|
||||
fig, ax = plt.subplots(figsize=(15, 9))
|
||||
df.plot('rho_300', 'T_c', kind='scatter', ax=ax)
|
||||
|
||||
for k, v in df.iterrows():
|
||||
ax.annotate(v['element'], (v['rho_300'], v['T_c']))
|
||||
|
||||
#fig.show()
|
||||
fig.savefig('/home/kvkempen/Documents/20212022Q3/Superconductivity/assignments/sc_elements.pdf')
|
||||
plt.close(fig)
|
||||
|
||||
@ -1,37 +1,37 @@
|
||||
\begin{tabular}{lrrll}
|
||||
\toprule
|
||||
Element & $T_c (\si{\kelvin})$ & $\rho_{300 K} (\si{\nano\ohm\meter})$ & Source $T_c$ & Source $\rho_{300 K}$ \\
|
||||
Element & $T_c (\si{\kelvin})$ & $\rho_{300 K} (\si{\nano\ohm\meter})$ & Source $T_c$ & Source $\rho_{300 K}$ \\
|
||||
\midrule
|
||||
Nb & 9.2500 & 152.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Tc & 8.2000 & 200.00 & \cite{webb} & \cite{rhowiki} \\
|
||||
Pb & 7.2000 & 213.00 & \cite{webb} & \cite{crc} \\
|
||||
La & 6.0000 & 615.00 & \cite{webb} & \cite{crc} \\
|
||||
V & 5.4000 & 202.00 & \cite{webb} & \cite{crc} \\
|
||||
Ta & 4.4000 & 135.00 & \cite{webb} & \cite{crc} \\
|
||||
Hg & 4.1500 & 961.00 & \cite{webb} & at 298 K \cite{crc} \\
|
||||
Sn & 3.7000 & 115.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
In & 3.4000 & 80.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Tl & 2.4000 & 150.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Re & 1.7000 & 172.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Th & 1.4000 & 147.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Pa & 1.4000 & 108.00 & \cite{webb} & \cite{crc} \\
|
||||
U & 1.3000 & 280.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Al & 1.1800 & 27.33 & \cite{webb} & \cite{crc} \\
|
||||
Ga & 1.0800 & 136.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Am & 1.0000 & 689.00 & \cite{webb} & \cite{rhowiki} \\
|
||||
Mo & 0.9200 & 55.20 & \cite{webb} & \cite{crc} \\
|
||||
Zn & 0.8500 & 60.60 & \cite{webb} & \cite{crc} \\
|
||||
Os & 0.7000 & 81.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Zr & 0.6000 & 433.00 & \cite{webb} & \cite{crc} \\
|
||||
Cd & 0.5200 & 68.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Ru & 0.5000 & 71.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Ti & 0.5000 & 390.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Hf & 0.3800 & 340.00 & \cite{webb} & \cite{crc} \\
|
||||
Ir & 0.1000 & 47.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Lu & 0.1000 & 582.00 & \cite{webb} & \cite{crc} \\
|
||||
Be & 1440.0000 & 37.60 & \cite{webb} & \cite{crc} \\
|
||||
W & 0.0100 & 54.40 & \cite{webb} & \cite{crc} \\
|
||||
Li & 0.0004 & 95.50 & \cite{webb} & \cite{crc} \\
|
||||
Rh & 0.0003 & 43.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Nb & 9.2500 & 152.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Tc & 8.2000 & 200.00 & \cite{webb} & \cite{rhowiki} \\
|
||||
Pb & 7.2000 & 213.00 & \cite{webb} & \cite{crc} \\
|
||||
La & 6.0000 & 615.00 & \cite{webb} & \cite{crc} \\
|
||||
V & 5.4000 & 202.00 & \cite{webb} & \cite{crc} \\
|
||||
Ta & 4.4000 & 135.00 & \cite{webb} & \cite{crc} \\
|
||||
Hg & 4.1500 & 961.00 & \cite{webb} & at 298 K \cite{crc} \\
|
||||
Sn & 3.7000 & 115.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
In & 3.4000 & 80.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Tl & 2.4000 & 150.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Re & 1.7000 & 172.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Th & 1.4000 & 147.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Pa & 1.4000 & 108.00 & \cite{webb} & \cite{crc} \\
|
||||
U & 1.3000 & 280.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Al & 1.1800 & 27.33 & \cite{webb} & \cite{crc} \\
|
||||
Ga & 1.0800 & 136.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Am & 1.0000 & 689.00 & \cite{webb} & \cite{rhowiki} \\
|
||||
Mo & 0.9200 & 55.20 & \cite{webb} & \cite{crc} \\
|
||||
Zn & 0.8500 & 60.60 & \cite{webb} & \cite{crc} \\
|
||||
Os & 0.7000 & 81.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Zr & 0.6000 & 433.00 & \cite{webb} & \cite{crc} \\
|
||||
Cd & 0.5200 & 68.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Ru & 0.5000 & 71.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Ti & 0.5000 & 390.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Hf & 0.3800 & 340.00 & \cite{webb} & \cite{crc} \\
|
||||
Ir & 0.1000 & 47.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
Lu & 0.1000 & 582.00 & \cite{webb} & \cite{crc} \\
|
||||
Be & 0.0260 & 37.60 & \cite{schmidt} (but \cite{webb} reports 1440 K) & \cite{crc} \\
|
||||
W & 0.0100 & 54.40 & \cite{webb} & \cite{crc} \\
|
||||
Li & 0.0004 & 95.50 & \cite{webb} & \cite{crc} \\
|
||||
Rh & 0.0003 & 43.00 & \cite{webb} & at 273 K \cite{crc} \\
|
||||
\bottomrule
|
||||
\end{tabular}
|
||||
|
||||